Lumirror characteristics
| Properties |
Item |
Typical values |
Measurement method |
| Mechanical properties |
Breaking strength(MD) |
215MPa |
JIS C2151 |
| Break elongation(MD) |
170％ |
JIS C2151 |
| Young's modulus |
4GPa |
ASTM D882 |
| Edge tear resistance |
220N/20mm |
JIS C2151 |
| Electrical properties |
Dielectric breakdown voltage |
300KV/mm |
JIS C2151 |
| Permittivity |
1KHz |
3.3 |
JIS C2151 |
| 1MHz |
3.2 |
| Dissipation factor |
1KHz |
0.20％ |
JIS C2151 |
| 1MHz |
1.0％ |
| Volume resistivity |
1017Ω・cm |
JIS C2151 |
| Surface specific resistance |
1017Ω・□ |
JIS K6911 |
| Physical properties |
Density |
1.40 /cm3 |
JIS K6760 |
| Melting point |
260℃ |
JIS K7121 |
| Temperature range where use and processing are possible |
-70- +180℃ |
- |
| Water absorption rate |
0.4％ |
Federl Test Method Std.No.406 |
| Temperature expansion coefficient |
1.2×10-5cm/cm/％RH |
- |
| Thermal deformation temperature |
- |
- |
| Flammability |
94VTM-2 |
UL |
| Thermal expansion coefficient |
1.5×10-6cm/cm/℃ |
ASTM D696 |
| Thermal shrinkage(MD) |
1.2％(150°C×30 mins.) |
JIS C2151 |
| Moisture vapor transmission rate |
6.9/m2/24hr/0.1mm |
JIS Z0208 |
| Oxygen transmission rate |
19cc(MPT)/m2/24hr/0.1mm/atm |
ASTM D1434 |
| Index of refraction |
1.60 |
ASTM D542 |
| Full light transmittance |
85％ |
JIS K6714 |
Note: The numeric values above are typical values. They are not standard values.